Type |
Standard Cure |
Maximum Cure Temperature |
Low Temperature Cure Option |
Outlife at R.T | Maximum Service Temperature |
Lap Shear Strength* |
Climbing Drum Peel Strength |
Features/Comments |
| VTA260 | 80°C for 5 hours |
120°C | 65°C for 16 hours |
21 days | 80°C | 30MPa | 55Nm/m | Adhesion of VTM260 series resin to cores. |
| MTA240 | 135°C for 1 hour | 175°C | 80°C for 5 hours | 30 days | 130°C | 40MPa | 100Nm/m | Structural film adhesive for bonding of metal/metal, metal/honeycomb composite. Co-cures with MTM® prepregs. |
| MTA263 | 120°C for 1 hour |
N/A | 80°C for 10 days | 30 days | 90°C | 32 MPa | 75Nm/m | Structural film adhesive for bonding of metal to metal, metal to honeycomb composite. Co-cures with MTM® prepregs. |
| 180°C for 1 hour |
N/A | 130°C for 4 hours |
30 days | 180°C | 33 MPa | 90Nm/m | Controlled flow for excellent honeycomb bonding and high peel strength. |